PROPERTIES

 N21

 N31

 NAP2

 NAP4

 LASER PROPERTIES

 Nd₂O₃ (wt%)

 2.2

 2.2

 1.0

 1.0

 Nd³⁺ conc. (10²⁰ions/cm³)

 2.68

 2.26

 3.70

 3.20

 Cross section for stimulated emission(10-20cm2)

 3.4±0.3

 4.0±0.3

 Fluorescence life time (usec)

 330

 340

 360

 380

 Fluorescence half-line width at 290ºK(Å)

 240

 201

 250

 270

 Center lasing wavelength (nm)

 1053

 1053

 1054

 1052

 OPTICAL PROPERTIES

 Non-linear refractive index coeff.n₂(×10^－13e.s.u)

 1.3

 1.1

 1.22

 1.1

 n (1053nm)

 1.5652

 1.528

 1.536

 1.523

 n_d

 1.5758

 1.5357

 1.542

 1.530

 n_F

 1.5731

 1.5413

 1.548

 1.536

 n_c

 1.582

 1.5332

 1.541

 1.527

 Abbe value

 65.3

 66.2

 67

 66

 dn/dT (10^-6/ºC) (20~100ºC)

 -4.2

 -4.3

 -8.7

 1.9

 Coeff.of linear thermal expansion (10^-6/ºC) (20~100ºC)

 11

 10.7

 8.2

 6.8

 Thermal coeff. of optical path (10^-6/ºC) (20~100ºC)

 1.9

 1.4

 3.6

 5.0

 THERMAL PROPERTIES

 Transformation temp.(ºC)

 500

 430

 478

 545

 Softening temp.(ºC)

 530

 475

 517

 620

 Coeff. of linear thermal expansion (10-6/ºC) (100~TgºC)

 12

 12.7

 9.6

 7.5

 Thermal conductivity (25ºC) (10^-3W/cmºC)

 5.53

 5.58

 7.66

 8.64

 Specific heat (25ºC) (J/cm³ºC)

 0.75

 0.75

 0.757

 0.753

 CHEMICAL PROPERTIES

 D_w (H2O 100ºC 1hr)(wt. Loss%)

 0.06

 0.09

 0.0137

 0.0007

 D_A (HNO₃ pH2.2 100ºC 1hr) (wt. loss%)

 0.3

 0.4

 OTEHER PROPERTIES

 Density(g/cm³)

 3.4

 2.83

 2.76

 2.58

 Young’s modulus (kgf/mm²)

 5640

 5270

 Posson’s ratio

 0.27

 0.27

 382

 549

 Knoop hardness (kg/cm²)

 650

 630